PTFE D05 pigment 57 Shore D turquoise Compound

PTFE turquoise has very good sliding properties, has best chemical resistance and is non-flammable. Due to its low elasticity it is not suitable for high mechanical loads. Note that due to the pigments it has higher strength than PTFE virgin.

Send an email

Description

Technical Specifications

Properties	Condition	Standard	Unit		Unit
Color						turquoise
Hardness	23°C/3sec. 23°C/15sec.	IS0 868	Shore D	57 ± 3 53 ± 5	Shore D	57 ± 3 54 ± 3
Tensile strength	23°C	ASTM D 4745-11a	MPa	≥ 31	psi	≥ 4495
Elongation at break	23°C	ASTM D 4745-11a	%	≥ 270	%	≥ 270
Compressive strength	23°C	DIN 53455	MPa	≥ 4	psi	≥ 580
Density/specific gravity	23°C	DIN 53479	kg/m³	2170	g/cm³	2,17
Ball indentation hardness	23°C	DIN 53456	MPa	28±5	psi	4060±725
Thermal conductivity		DIN 52612		≥ 0,8		≥ 0,8
Coefficient of thermal expansion	25℃-200℃			≥ 19		≥ 19
Coefficient of friction	23°C		µ	≥ 0,08	µ	≥ 0,08
Young's modulus	23°C	DIN 53455	MPa	≥ 540	psi	≥ 78500
Minimum service temperature			℃	-200	°F	-328
Maximum service temperature			℃	260	°F	500